The specification of this wire posted on the website, its chemical composition, and technological parameters have not yet been approved by the specialists of our company. If you are interested, please contact us.
|
NAME
|
CLASSIFICATION INDEXES
|
TUU 28.7-31749248.002-2002
(suspended)
|
|
FCWw-TMW10
|
Diametr: 1,6–2,4 mm Protection: self-shielding
Design: tubular, overlapping
|
Purpose and scope
Полуавтоматическая сварка металлоконструкций из низкоуглеродистых и низколегированных сталей марок Ст3, Ст4, Ст5, 10, 15, 20, 09Г2С, 17ГС, 10Г2С1 преимущественно в условиях монтажа и открытых цехов толщиной более 5 мм.
Welding and technological properties
-
Arc Stability - consistent and stable arc behavior, good weld bead appearance. The wire provides deep penetration of the base metal. Slag completely covers the weld bead, and easy to remove slag. High crack and pore resistance. High wind resistance
Welding technology
-
Welding in the lower position is performed at the location of the wire perpendicular to the weld bead or tilt «angle back». Welding of vertical joints is possible with the “bottom-up” and “top-down” methods with the wire positioned “forward angle” or perpendicular to the joint.
-
When welding angular joints with a leg more than 8 mm, transverse oscillations of the wire are obligatory.
-
Use DC reverse polarity.
Deposit composition (Weld metal), %
| C | Si | Mn | Ni | Al | S |
| ≤0.2 | ≤0.5 | 1.1 | 1.0 | ≤0.02 | ≤0.02 |
_
Welding Alloys Analog
| Brand of the wire |
Distance, % |
virobnik | C | Mn | Si | Ni | Mo |
| ROBOFIL R Ni1SR (60) | 0.22 | Welding Alloys | 0.06 | 1.2 | 0.4 | 0.9 | |
| ROBOFIL M Ni1 (61) | 0.29 | Welding Alloys | 0.05 | 1.3 | 0.6 | 0.9 | |
| ROBOFIL B Ni1 (62) | 0.36 | Welding Alloys | 0.06 | 1.4 | 0.4 | 1.1 | |
| ROBOFIL B NiMo (65) | 0.57 | Welding Alloys | 0.05 | 1.4 | 0.4 | 1.2 | 0.4 |
| ROBOFIL M NiMo (64) | 0.86 | Welding Alloys | 0.05 | 1.6 | 0.4 | 1.6 | 0.3 |
Typical mechanical properties of the weld metal
|
Ultimate tensile strength, MPa |
Yield Strength, MPa |
Elongation (l = 5×d), % |
Impact strength, KCV, J/cm2 at T °C |
|
minimum
|
+20°
|
-20°
|
-40°
|
|
480-590 |
400 |
20 |
≥80 |
≥40 |
- |
Modes of the welding process
|
Wire diameter, mm
|
Current, A
|
Voltage, V
|
Wire overhang, mm
|
|
1,6-1,8
|
120-250
|
22-26
|
20-30
|
|
2,0-2,2
|
160-300
|
23-27
|
20-40
|
|
2,4
|
200-350
|
24-28
|
20-40
|
Weld Positions
Ø 1,6-1,8 мм:
Ø 2,0-2,2 мм:
Ø 2,4 мм:
Delivery type (More)
|
The diameter of the wire
|
1,2–2,0 mm
|
2,4–3,2 mm
|
1,6–6,0 mm
|
|
Delivery |
Magazine
B-300; S-300
|
Molded Bay
|
Bay
|
|
Standard package |
cardboard box |
cartons |
metal drums |
metal drums |
|
Weight, kg |
10-15
|
20-55
|
50-70
|
50-70
|