Flux-cored Strips

  1. Product name
  2. The Formation of the weld bead
  3. Separation of Slag
  4. Deposition Rate, kg/h
  5. Addiction Weld metal Cracking
  6. Consumption per 1 kg of wire Weld metal, kg
  7. Weld metal Hardness (HRC for 3rd-4th layer, unless otherwise stated)

123456
FCS-AS101

Ø16,5х4,2
-
-
-
rutile
various
after surfacing
50-56
self-shielded flux-cored strip is designed for depositing by mechanized open arc and submerged arc welding processes a layer of a high-chromium wear-resistant alloy of «Sormite-l» type on parts working under conditions of intensive abrasion wear at normal and high temperatures. DCRP (direct current reverse polarity) is recommended. The strip is used for hardfacing blast-furnace charging systems, coke mill rolls, beaters, gyratory crusher liners, armour plates, chutes, conveyor pans, bulldozer blades, etc.
[C: 2.7; Cr: 26.0; Mn: 1.3; Ni: 4.0; Si: 3.2; S: <0.07; P: <0.08; ]
FCS-TMW634

Ø16,5х4,2
MF 10-GF-60-
-
-
metal cored
self- shielding
after surfacing
56-62
Наплавка абразивностойкого коррозионностойкого слоя при рабочих температурах до 450 °С. Металл обладает высокой абразивной стойкостью в условиях высоких температур с умеренными ударами. Рекомендуется для наплавки футеровки конусных дробилок, контактных зон загрузочных конусов доменных печей, пластин лотков загрузочных механизмов доменных печей, плакирования стальных биметаллических листов и т.п.
[C: 4.5; Si: <1.0; Cr: 32.0; Mo: 1.0; S: 0.02; P: 0.02; ]
FCS-TMW635

Ø16,5х4,2
MF 10-GF-65-
-
-
metal cored
self- shielding
after surfacing
56-60
Наплавка абразивностойкого коррозионностойкого слоя при рабочих температурах до 450 °С. Металл обладает высокой абразивной стойкостью в условиях высоких температур с умеренными ударами. Для наплавки ножей бульдозеров и грейферов. плакирования стальных биметаллических листов и т.п.
[C: 4.5; Si: <1.0; Cr: 30.0; Mn: <1.0; S: 0.02; P: 0.02; ]
FCS-TMW636

Ø16,5х4,2
MF 10-GF-60-
-
-
metal cored
self- shielding
after surfacing
60-64
Наплавка абразивностойкого коррозионностойкого слоя при рабочих температурах до 450 °С. Металл обладает высокой абразивной стойкостью в условиях высоких температур с умеренными ударами. Рекомендуется для наплавки ножей бульдозеров и грейферов, плакирования стальных биметаллических листов и т.п.
[C: 4.0; Si: <1.0; Cr: 30.0; Mn: <1.0; V: ≤1.0; Ni: ≤1.0; B: 1.0; S: 0.02; P: 0.02; ]
FCS-TMW637

Ø16,5х4,2
MF 10-GF-65-
-
-
metal cored
self- shielding
after surfacing
60-64
The strip is designed for depositiong by the automated open arc welding process a high alloyed wear-resistant weld metal on steel parts and plates exposed to severe mineral abrasion combined with moderate impact. The strip is used for hardfacing protective sheets of mining equipment and quarry machinery of various purposes. (450 °С)
[C: 4.0; Si: <1.0; Cr: 27.0; Mn: <1.0; Ni: ≤1.5; B: 2.0; S: 0.02; P: 0.02; ]
FCS-TMW638

Ø16,5х4,2
MF 10-GF-65-
-
-
metal cored
self- shielding
after surfacing
60-64
Наплавка абразивностойкого коррозионностойкого слоя при рабочих температурах до 650 °С. Металл обладает высокой абразивной стойкостью в условиях высоких температур с умеренными ударами. Рекомендуется для наплавки конусов доменных печей, ремонта оборудования аглофабрик, конуса доменных печей, плиты и валки дробилок минералов, плакирования стальных биметаллических листов.
[C: 3.5; Si: <1.0; Mn: <1.0; Cr: 22.0; Nb: 6.0; Mo: 5.0; W: 2.0; S: 0.02; P: 0.02; ]

Select the sorting method:
Hardness descendingHardness ascending
Propensity weld metal cracking




>