Flux-cored wires for welding TM.WELTEC Ltd.

  1. Product Name
  2. Ultimate tensile strength, MPa
  3. Yield Strength, MPa
  4. Elongation (l = 5×d)
  5. Charpy V-Notch, KCV, J/cm2 at T °C
  6. Deposit composition (Weld metal), %
* Wires sorted in alphabetical order

Select All
Unselect All
Compare selected wires

V123456
PP_ANCh2
T C FeC-2-N-3
ECI-B
160-200350-410-C: 4.0; Si: 3.2; Mn: 0.4; Ti: 0.9; Al: 0.5; S: 0.007; P: 0.016;
PP_ANCh5350-510300-4204-9+20°: ≥40C: 3.5; Si: 3.0; Mn: 0.4; S: ≤0.01; P: ≤0.04; Ca: ≤0.1; Mg: ≤0.1;
BeT_PPc_TMB14
T Cr Mo1 R С
E81T1-B2-H4
50043022+20°: ≥100; :  ≥80; -30°: ≥80C: 0.06; Si: 0.3; Mn: 0.8; Cr: 1.0; Mo: 0.5; S: ≤0.03; P: ≤0.03;
BeT_PPc_TMB15
Т Cr Mo1 R C
E81T1-B2-H4
49034018+20°: ≥80; :  ≥60; -20°: ≥40C: 0.06; Si: 0.3; Mn: 0.8; Cr: 1.0; Mo: 0.5; V: 0.2; S: 0.014; P: 0.012;
PPc_TMV10480-59040020+20°: ≥80; -20°:  ≥40C: ≤0.2; Si: ≤0.5; Mn: 1.1; Ni: 1.0; Al: ≤0.02; S: ≤0.02;
PPc_TMV10N
Т 42 2 Y N 2
E71T-H4
550-62042016+20°: ≥70; -20°:  ≥35; -40°C: 0.08; Si: 0.2; Mn: 1.1; Ni: 1.0; Al: 1.0; S: ≤0.02;
WELTEC_H210Y
Т CrMn20 U N 3
EСrMnT0-3
500-69036020+20°: ≥80; -20°:  ≥60C: 0.1; Si: 0.2; Mn: 20.0; S: ≤0.025; P: ≤0.025; Ti: 0.1; Cr: 9.0;
WELTEC_H215
Т 18 8 Mn U N 3
E307T0-3
550-59036030+20°: ≥80; -60°:  ≥60; C: 0.08; Si: 0.5; Cr: 19.0; Mn: 6.0; Ni: 9.0; S: ≤0.025; P: ≤0.025;
BeT_PPv_TMB11
Т CrNiMn15 U N 3
ECrNiMn15T0-3
520360-40030+20°: ≥70; -40°:  ≥50; C: 0.1; Si: 0.1; Mn: 15.0; Ni: 9.0; S: ≤0.025; P: ≤0.025; Cr: 10.0;
BeT_PPc_TMB4
T 42 3 R C2
49041022+20°: ≥100; :  ≥80; -30°: ≥50C: 0.07; Si: 0.35; Mn: 1.2; S: ≤0.03; P: ≤0.03;
PP_AN1
Т 35 A V N 1 H15
E61T-1 H16
460-50035016+20°: 35C: 0.08; Si: 0.1; Mn: 0.8; S: ≤0.04; P: ≤0.04;
PP_AN4
T 42 3 R C2
51042022+20°: ≥110; :  ≥90; -30°: ≥60C: 0.06; Si: 0.25; Mn: 1.1; S: ≤0.03; P: ≤0.03;
PP_AN8
T 42 2 Р С 2 Н10
AWS A5.36: E71T1-C1A0-CS2-H8
50040020+20°: ≥90; :  ≥60; -20°: ≥35C: ≤0.12; Si: 0.25; Mn: 1.2; S: ≤0.03; P: ≤0.03;
PP_ANT540-65044022+20°: ≥80; -20°:  ≥45C: 0.08; Si: 0.3; Mn: 1.4; Ni: 0.7; S: ≤0.03; P: ≤0.03;
FCWw-ASTs59044016: ; -20°:  ≥35; C: ≤0,12; Si: 0.4; Mn: 1.0; Ni: 0.8; Al: ≤1.5; S: ≤0.03; P: ≤0.03;
FCWw-TMW-mc5
T 42 2 M M 1 H10
A5.18: E70C-6C
52042024+20°: ≥160; -20°:  ≥100; -40°: ≥80C: ≤0.06; Si: 0.45; Mn: 1.5; S: ≤0.02; P: ≤0.02;
PPc_TMV1
Т 35 A Z N3
460-55033016+20°: 40C: 0.08; Si: 0.1; Mn: 0.8; S: ≤0.035; P: ≤0.035;
PPc_TMB2
Т 42 0 P C3
E710-1C
56044016+20°: ≥60; :  ≥35C: 0.07; Si: 0.08; Mn: 0.4; S: ≤0.03; P: ≤0.03;
FCWw-TMW210
Т Z P N 3
620-660370-39022-30+20°: 110; -20°:  60; -40°: 45C: 0.09; Si: 0.24; Mn: 17.5; Cr: 9.5; S: 0.003; P: 0.015; Ti: 0.08;
PPc_TMB29
Т 42 3 R С1
49042022+20°: ≥80; -40°: ≥35C: 0.08; Si: 0.3; Mn: 1.3; S: ≤0.03; P: ≤0.03;
PPc_TMV3
Т 38 2 W N3
500-59038020+20°: ≥80; -20°:  ≥35C: 0.1; Si: 0.08; Mn: 1.1; Ni: 0.6; Al: 0.6; S: ≤0.03; P: ≤0.03; Ti: 0.2;
FCWw-TMW5
AWS/SFA 5.20
58044024+20°: ≥120; -20°:  60C: 0.05; Si: 0.35; Mn: 1.4; S: 0.016; P: 0.018;
PPc_TMV6
T 42 0 Z N 3 Н10
E70T-4
520-62044020+20°: ≥80; :  ≥60C: ≤0.12; Si: 0.3; Mn: 1.0; Al: 0.1; Ti: 0.2; S: ≤0.03; P: ≤0.03;
PPc_TMV7
T 42 4 Р С 1 Н5
E71T1-C1A4-CS2-H4
49040022+20°: ≥120; -20°:  ≥90; -40°: ≥70C: ≤0.12; Si: 0.4; Mn: 1.3; S: ≤0.03; P: ≤0.03;
PPc_TMB8
Т 38 0 P C1
E71T-1C H4
55045020+20°: ≥100; -20°:  ≥80; -30°: ≥50C: 0.08; Si: 0.3; Mn: 1.2; S: ≤0.035; P: ≤0.035;
PPc_EK148036018+20°: ≥50; -20°:  ≥35C: 0.03; Si: 0.03; Mn: 0.1; Ni: 1.2; S: ≤0.03; P: ≤0.03;
PPc_EK248036018+20°: ≥35C: 0.03; Si: 0.03; Mn: 0.15; S: ≤0.03; P: ≤0.03;

     Flux-cored wires for welding cast iron
     Flux-cored wires for welding alloy, high strength and heat-resistant steels
     Flux-cored wires for welding dissimilar steels and difficult-weldable steels
     Flux-cored wires for welding carbon and low alloy steels


Select the sorting method:
Tensile ascendingYield ascending
Elongation ascendingtoughness at +20 ° C ascending
The number of carbon (C) ascendingThe amount of manganese (Mn) Ascending
Amount of nickel (Ni) ascendingAmount of chromium (Cr) ascending
Wires sorted in alphabetical order

>