Counterbodies: Hot metal (steel, nickel alloys, copper, etc.).

Additional conditions: oxidizing atmosphere, bumps

Examples: Nadelki forging hammers and presses, forging dies hot stamping


  1. Product name
  2. EN 14 700, DIN 8555
  3. Accordance with the analogues («TM.ESAB», «TM.BÖHLER», «TM.WELDING ALLOYS»)
  4. Type, Shield
  5. Weld metal Hardness (HRC for 3rd-4th layer, unless otherwise stated)
  6. Deposit composition (Weld metal), %
* Wires sorted in alphabetical order
123456
WELTEC-H295-G

Ø3,0–4,0
T Fe11
MF9-GF-300-СNTZ
-
-
-
metal cored
shielding gas
after surfacing
26-37
after work hardening
48-60
Порошковая проволока марки ВЕЛТЕК-H295-G предназначена для наплавки в среде защитных газов уплотнительных поверхностей энергетической арматуры, а также супертяжелонагруженной кузнечно-штамповой оснастки горячего деформирования, работающей в условиях трения металла о металл, коррозионного и эрозионного износа при повышенных температурах до 1100˚С. Рекомендуется для наплавки на постоянном токе обратной полярности. Защита: газ M12 (98% Ar+2%CO2) или М13 (98% Ar+2%O2)
[C: 0.06; Mn: 1.1; Si: 1.0; Cr: 30.5; Ni: 9.5; Mo: 3.0; S: 0.012; P: 0.017; ]
WELTEC-H295-S

Ø3,0–4,0
T Fe11
MF9-GF-300-СNTZ
-
-
-
metal cored
flux
after surfacing
26-37
after work hardening
48-60
Порошковая проволока марки ВЕЛТЕК-H295-S предназначена для наплавки под флюсом уплотнительных поверхностей энергетической арматуры, а также супертяжелонагруженной кузнечно-штамповой оснастки горячего деформирования, работающей в условиях трения металла о металл, коррозионного и эрозионного износа при повышенных температурах до 1100˚С. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.06; Mn: 1.1; Si: 1.0; Cr: 30.5; Ni: 9.5; Mo: 3.0; S: 0.012; P: 0.017; ]
WELTEC-H460

Ø1,6-4,0
T Z Fe2
MF6-GF-450-GP
-
SK 500-G
-
metal cored
flux
after surfacing
41-52
Strengthening and recovering hard-facing of rolls for cycle rolling, rolls for tube mills, knifes for hot cutting, extrusion toolage and punching tools, scrapers of conveyor for shearing removal, forming rollers of coiling machines, rolls of flatting-mills and ball-rolling mills.
[C: 0.25; Mn: 0.8; Si: 0.9; Cr: 5.5; Mo: 1.2; V: 0.4; Ti: <0.6; S: <0.03; P: <0.03; ]
WELTEC-H460-G

Ø1,6-2,6
T Fe6
MF6-GF-450-GP
-
SK 500-G
-
metal cored
shielding gas
after surfacing
41-52
Порошковая проволока марки ВЕЛТЕК-Н460-G предназначена для механизированной наплавки в защитных газах деталей, работающих в условиях циклической термической нагрузки и интенсивного изнашивания. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.25; Mn: 0.8; Si: 0.9; Cr: 5.5; Mo: 1.2; V: 0.4; Ti: <0.6; S: <0.03; P: <0.03; ]
WELTEC-H460-O

Ø1,6-3,2
T Fe6
MF6-GF-450-GP
-
SK 500-G
-
rutile
self- shielding
after surfacing
41-52
Порошковая проволока марки ВЕЛТЕК-Н460-O предназначена для механизированной наплавки открытой дугой деталей, работающих в условиях циклической термической нагрузки и интенсивного изнашивания. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.25; Mn: 0.8; Si: 0.8; Cr: 5.1; Mo: 1.2; V: 0.4; Ti: 0.4; S: 0.013; P: 0.015; ]
WELTEC-H460-RMZ

Ø1,6–3,6
-
SK 500-G
-
metal cored
flux
after surfacing
45-51
Порошковая проволока марки ВЕЛТЕК-Н460-РМЗ предназначена для механизированной наплавки под флюсом деталей, работающих в условиях циклической термической нагрузки и интенсивного изнашивания. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.27; Mn: 0.7; Si: 1.1; Cr: 5.5; Mo: 1.2; V: 0.45; S: <0.04; P: <0.06; ]
WELTEC-H460-01-G

Ø2,0-2,6
T Fe7
MF5-GF-45-RTZ
-
-
-
metal cored
shielding gas
after surfacing
45-50
Repairing of punches for hot punching. Parent metal: steels of 5KhNM, 5KhNB and 38KhN3MBA grades.
[C: 0.15; Mn: 0.9; Si: 0.5; Cr: 12.0; Ni: 1.6; Mo: 2.0; V: 0.1; Nb: 0.1; S: <0.03; P: <0.03; ]
WELTEC-H460-01-O

Ø1,6-3,2
T Fe7
MF5-GF-45-RTZ
-
-
-
rutile
self- shielding
after surfacing
42-50
Порошковая проволока марки ВЕЛТЕК-Н460.01-O предназначена для механизированной наплавки открытой дугой деталей, работающих в условиях циклической термической нагрузки, больших удельных давлений при повышенных температурах. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.15; Mn: 0.9; Si: 0.5; Cr: 12.0; Ni: 1.6; Mo: 2.0; V: 0.1; Nb: 0.1; S: <0.03; P: <0.03; ]
WELTEC-H460-01-S

Ø1,6-6,0
T Fe7
MF5-GF-45-RTZ
-
-
-
metal cored
flux
after surfacing
42-50
Порошковая проволока марки ВЕЛТЕК-Н460.01-S предназначена для механизированной наплавки под флюсом деталей, работающих в условиях циклической термической нагрузки, больших удельных давлений при повышенных температурах. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.15; Mn: 0.9; Si: 0.5; Cr: 12.0; Ni: 1.6; Mo: 2.0; V: 0.1; Nb: 0.1; S: <0.03; P: <0.03; ]
WELTEC-H460-02-G

Ø1,6-2,6
T Fe3
MF3-GF-45-GP
-
-
-
metal cored
shielding gas
after surfacing
42-52
Порошковая проволока марки ВЕЛТЕК-Н460.02-G предназначена для механизированной наплавки в защитных газах деталей, работающих в условиях циклической термической нагрузки и интенсивного изнашивания при нормальных и повышенных температурах. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.25; Mn: 1.0; Si: 0.3; Cr: 2.5; Ni: 1.0; Mo: 2.5; V: 0.3; Nb: 0.1; S: <0.03; P: <0.03; ]
WELTEC-H460-02-O

Ø1,6-3,2
T Fe3
MF3-GF-45-GP
-
-
-
rutile
self- shielding
after surfacing
42-52
Порошковая проволока марки ВЕЛТЕК-Н460.02-O предназначена для механизированной наплавки открытой дугой деталей, работающих в условиях циклической термической нагрузки и интенсивного изнашивания при нормальных и повышенных температурах. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.25; Mn: 1.0; Si: 0.3; Cr: 2.5; Ni: 1.0; Mo: 2.5; V: 0.3; Nb: 0.1; S: <0.03; P: <0.03; ]
WELTEC-H460-02-S

Ø2,0-3,6
T Z Fe7
MF3-GF-45-GP
-
-
-
metal cored
flux
after surfacing
40-50
Hard-facing of rolls for cold rolling of reinforcement rods, blades for cold cutting, die blocks and die punches for cold forming and pressing. The deposited metal has high wear-resistance in conditions of high specific pressures and metallic friction.
[C: 0.25; Mn: 1.0; Si: 0.3; Cr: 2.5; Ni: 1.0; Mo: 2.5; V: 0.3; Nb: 0.1; S: <0.03; P: <0.03; ]
WELTEC-H460-03

Ø2,0–3,6
-
-
-
-
various
after surfacing
56-60
Порошковая проволока марки ВЕЛТЕК-Н460.03 предназначена для механизированной наплавки под флюсом и в среде защитных газов деталей, работающих в условиях трения металла о металл при нормальных и повышенных температурах. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.8; Mn: 0.8; Si: 0.8; Cr: 4.5; Mo: 2.0; V: 0.4; S: <0.03; P: <0.03; ]
WELTEC-H460-04

Ø2,0–3,6
-
-
-
-
various
after surfacing
40-48
Порошковая проволока марки ВЕЛТЕК-Н460.04 предназначена для механизированной наплавки под флюсом и в среде защитных газов деталей, работающих в условиях трения металла о металл при нормальных и повышенных температурах. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.3; Mn: 0.8; Si: 0.8; Cr: 11.5; V: 0.3; Ti: <0.4; W: 4.5; S: <0.04; P: <0.04; ]
WELTEC-H460-05

Ø1,6–3,6
-
-
-
-
various
after surfacing
46-52
>Порошковая проволока марки ВЕЛТЕК-Н460.05 предназначена для механизированной наплавки под флюсом и в среде защитных газов деталей, работающих в условиях трения металла о металл при нормальных и повышенных температурах. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.22; Mn: 0.7; Si: 0.7; Cr: 9.5; Mo: 2.0; V: <0.2; Nb: <0.1; W: <0.3; S: <0.04; P: <0.04; ]
WELTEC-H460K

Ø1,6–3,6
-
SK 500-G
-
metal cored
flux
after surfacing
41-52
Порошковая проволока марки ВЕЛТЕК-Н460К предназначена для механизированной наплавки под флюсом деталей, работающих в условиях циклической термической нагрузки и интенсивного изнашивания. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.25; Mn: 1.4; Si: 0.9; Cr: 5.4; Mo: 1.2; V: 0.4; Ti: <0.2; S: <0.04; P: <0.04; ]
WELTEC-H465

Ø3,0–6,0
OK Tubrodur 15.52 - с.н. ОК Tubrodur 58 O/GМ - н.н.*
-
HARDFACE R58
-
flux
after surfacing
42-51
>Порошковая проволока марки ВЕЛТЕК-Н465 предназначена для механизированной наплавки под флюсом деталей, работающих в условиях трения металла о металл при повышенных температурах, термоциклировании и больших удельных давлениях. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.3; Mn: 0.8; Si: 1.1; Cr: 7.0; Mo: 2.5; V: <0.2; Ni: <0.5; Ti: <0.6; S: <0.04; P: <0.04; ]
WELTEC-H480-G

Ø1,6-2,0
T Z Fe3
MF3-GF-50-GP
-
-
HARDFACE WMOLC
metal cored
shielding gas
after surfacing
47-53
Hard-facing of rolls for hot rolling, punches for press equipment, large bell rods, parts of stripping mills. The wire provides higher heat-, wear- and flame erosion resistance.
[C: 0.3; Mn: 1.1; Si: 0.8; Cr: 4.0; Mo: 1.5; V: 0.4; W: 2.5; Ti: <0.6; S: <0.03; P: <0.03; ]
WELTEC-H480-O

Ø1,6-2,0
T Z Fe3
MF3-GF-50-GP
-
-
HARDFACE WMOLC
metal cored
self- shielding
after surfacing
47-53
Hard-facing of rolls for hot rolling, punches for press equipment, large bell rods, parts of stripping mills. The wire provides higher heat-, wear- and flame erosion resistance.
[C: 0.3; Mn: 1.1; Si: 0.8; Cr: 4.0; Mo: 1.5; V: 0.4; W: 2.5; Ti: <0.6; S: <0.03; P: <0.03; ]
WELTEC-H480-S

Ø3,0-4,0
T Z Fe3
MF3-GF-50-GP
-
-
HARDFACE WMOLC
metal cored
flux
after surfacing
47-53
Hard-facing of rolls for hot rolling, punches for press equipment, large bell rods, parts of stripping mills. The wire provides higher heat-, wear- and flame erosion resistance.
[C: 0.3; Mn: 1.1; Si: 0.8; Cr: 4.0; Mo: 1.5; V: 0.4; W: 2.5; Ti: <0.6; S: <0.03; P: <0.03; ]
WELTEC-H480K

Ø1,6–3,6
-
-
HARDFACE WMOLC
metal cored
flux
after surfacing
47-53
Порошковая проволока марки ВЕЛТЕК-Н480 предназначена для автоматической наплавки деталей, работающих в условиях трения металла о металл при повышенных температурах, термоциклировании и больших удельных давлениях. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.35; Mn: 1.1; Si: 0.8; Cr: 4.0; Mo: 1.7; V: 0.35; W: 2.5; S: <0.04; P: <0.04; ]
WELTEC-H480NT

Ø2,4–4,0
T Z Fe3
MF3-GF-50-GPT
-
-
-
metal cored
flux
after surfacing
46-53
Hard-facing of gauges for pipe-mills, knifes for hot cutting. The wire provides higher heat- and wear-resistance and moderate flame erosion resistance.
[C: 0.3; Mn: 1.0; Si: 0.8; Cr: 5.5; Mo: 3.0; V: 0.5; W: 3.0; S: <0.03; P: <0.03; ]
WELTEC-H480NT-G

Ø1,6–2,6
T Z Fe3
MF3-GF-50-GPT
-
-
-
metal cored
shielding gas
after surfacing
46-53
Порошковая проволока марки ВЕЛТЕК-Н480НТ-G предназначена для автоматической наплавки деталей, работающих в условиях трения металла о металл при повышенных температурах, термоциклировании и больших удельных давлениях. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.3; Mn: 1.0; Si: 0.8; Cr: 5.5; Mo: 3.0; V: 0.5; W: 3.0; S: <0.03; P: <0.03; ]
WELTEC-H480NT-O

Ø1,6–3,2
T Z Fe3
MF3-GF-50-GPT
-
-
-
metal cored
self- shielding
after surfacing
46-53
Порошковая проволока марки ВЕЛТЕК-Н480НТ-O предназначена для автоматической наплавки деталей, работающих в условиях трения металла о металл при повышенных температурах, термоциклировании и больших удельных давлениях. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.3; Mn: 1.0; Si: 0.8; Cr: 5.5; Mo: 3.0; V: 0.5; W: 3.0; S: <0.03; P: <0.03; ]
WELTEC-H480S

Ø1,6–2,2
T Z Fe3
-
-
HARDFACE WMOLC
rutile
self- shielding
after surfacing
47-53
Hard-facing of rolls for hot rolling, punches for press equipment, large bell rods, parts of stripping mills, cores for dogging cranes. The wire provides high heat-, wear- and flame erosion resistance.
[C: 0.35; Mn: 1.1; Si: 0.8; Cr: 4.0; Mo: 1.7; V: 0.35; Ti: <0.6; W: 2.5; S: <0.04; P: <0.04; ]
WELTEC-H480S-S

Ø3,0–4,0
T Z Fe3
-
-
HARDFACE WMOLC
rutile
flux
after surfacing
47-53
Hard-facing of rolls for hot rolling, punches for press equipment, large bell rods, parts of stripping mills, cores for dogging cranes. The wire provides high heat-, wear- and flame erosion resistance.
[C: 0.35; Mn: 1.1; Si: 0.8; Cr: 4.0; Mo: 1.7; V: 0.35; Ti: <0.6; W: 2.5; S: <0.04; P: <0.04; ]
WELTEC-H500-RM

Ø3,0-4,0
T Fe3
MF3-GF-50-GPT
-
-
-
metal cored
flux
after surfacing
42-51
Hard-facing of rolls for hot rolling. The wire provides higher resistance to flame erosion and pin formation.
[C: 0.3; Mn: 0.9; Si: 0.8; Cr: 3.0; V: 0.3; W: 9.0; S: <0.03; P: <0.03; ]
WELTEC-H500-RM-G

Ø1,6-2,4
T Fe3
MF3-GF-50-GPT
-
-
-
metal cored
shielding gas
after surfacing
42-51
Hard-facing of rolls for hot rolling. The wire provides higher resistance to flame erosion and pin formation.
[C: 0.3; Mn: 0.9; Si: 0.8; Cr: 3.0; V: 0.3; W: 9.0; S: <0.03; P: <0.03; ]
WELTEC-H500-RMZ

Ø3,0–6,0
-
-
-
metal cored
flux
after surfacing
47-53
Порошковая проволока марки ВЕЛТЕК-Н500-РМЗ предназначена для автоматической наплавки под флюсом деталей из углеродистых и низколегированных сталей, работающих в условиях трения металла о металл при повышенных температурах, термоциклировании и больших удельных давлениях. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.35; Mn: 0.85; Si: 0.6; Cr: 3.2; V: 0.35; W: 9.0; S: <0.04; P: <0.04; ]
WELTEC-H500-RMK

Ø2,6–6,0
-
-
-
metal cored
flux
after surfacing
42-51
Порошковая проволока марки ВЕЛТЕК-Н500-РМК предназначена для автоматической наплавки под флюсом деталей из углеродистых и низколегированных сталей, работающих в условиях трения металла о металл при повышенных температурах, термоциклировании и больших удельных давлениях. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.3; Mn: 1.2; Si: 0.8; Cr: 3.0; Ni: <0.7; V: 0.3; Mo: <0.3; W: 9.0; S: <0.04; P: <0.04; ]
WELTEC-H500-RMS

Ø2,6–6,0
-
-
-
metal cored
flux
after surfacing
45-54
Порошковая проволока марки ВЕЛТЕК-Н500-РМС предназначена для автоматической наплавки под флюсом деталей из углеродистых и низколегированных сталей, работающих в условиях трения металла о металл при повышенных температурах, термоциклировании и больших удельных давлениях. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.33; Mn: 0.8; Si: 0.6; Cr: 2.8; Ni: <0.7; V: 0.35; Mo: <0.3; W: 9.5; S: <0.04; P: <0.04; ]
WELTEC-H500-RMU

Ø2,6–6,0
-
-
-
metal cored
flux
after surfacing
35-45
Порошковая проволока марки ВЕЛТЕК-Н500-РМУ предназначена для автоматической наплавки под флюсом деталей из углеродистых и низколегированных сталей, работающих в условиях трения металла о металл при повышенных температурах, термоциклировании и больших удельных давлениях. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.17; Mn: 1.2; Si: 0.8; Cr: 2.5; Ni: <0.7; V: 0.3; Mo: <0.3; W: 8.0; S: <0.04; P: <0.04; ]
WELTEC-H505-RM

Ø3,0-6,0
T Fe4
MF3-GF-50-GPT
-
-
-
metal cored
flux
after surfacing
48-54
Hard-facing of rolls for hot rolling. The wire provides higher resistance to flame erosion and pin formation.
[C: 0.3; Mn: 0.9; Si: 0.8; Cr: 3.2; V: 0.3; W: 11.0; S: <0.03; P: <0.03; ]
WELTEC-H505-RM-G

Ø1,6-2,6
T Fe4
MF3-GF-50-GPT
-
-
-
metal cored
shielding gas
after surfacing
48-54
Порошковая проволока марки ВЕЛТЕК-Н505-РМ-G предназначена для автоматической наплавки под флюсом деталей из углеродистых и низколегированных сталей, работающих в условиях трения металла о металл при повышенных температурах, термоциклировании и больших удельных давлениях. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.3; Mn: 0.9; Si: 0.8; Cr: 3.2; V: 0.3; W: 11.0; S: <0.03; P: <0.03; ]
WELTEC-H550-RM

Ø2,4-3,6
T Z Fe3
MF3-GF-55-GPT
-
-
-
metal cored
flux
after surfacing
54-60
Hard-facing of rolls for hot rolling. The wire provides higher resistance to flame erosion and pin formation.
[C: 0.5; Mn: 0.9; Si: 0.8; Cr: 4.0; W: 9.0; V: 0.3; S: <0.03; P: <0.03; ]
WELTEC-H550-RM-G

Ø1,6-2,6
T Fe4
MF3-GF-55-GPT
-
-
-
metal cored
shielding gas
after surfacing
53-59
Порошковая проволока марки ВЕЛТЕК-Н550-РМ-S предназначена для автоматической наплавки под флюсом деталей из углеродистых и низколегированных сталей, работающих в условиях трения металла о металл при повышенных температурах, термоциклировании и больших удельных давлениях. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.5; Mn: 0.9; Si: 0.8; Cr: 4.0; W: 9.0; V: 0.3; S: <0.03; P: <0.03; ]
WELTEC-H565-G

Ø1,2-3,2
T Z Fe4
MF6-GF-55-GPT
-
-
HARDFACE W
metal cored
shielding gas
after surfacing
54-60
Strengthening and recovering of parts after abrasive and impact wear. Cutting edges for cold and hot processing, ripper and trimming dies, roller sheet-straighteners, rollers of mineral mills and stone-crushers, scrapers, crushing and grinding cones of mills, extrusion screws.
[C: 0.55; Mn: 1.4; Si: 0.7; Cr: 5.5; Mo: 1.5; W: 1.5; S: 0.014; P: 0.015; ]
WELTEC-H565-O

Ø1,2-3,2
T Z Fe4
MF6-GF-55-GPT
-
-
HARDFACE W
metal cored
self- shielding
after surfacing
54-60
Strengthening and recovering of parts after abrasive and impact wear. Cutting edges for cold and hot processing, ripper and trimming dies, roller sheet-straighteners, rollers of mineral mills and stone-crushers, scrapers, crushing and grinding cones of mills, extrusion screws.
[C: 0.55; Mn: 1.4; Si: 0.7; Cr: 5.5; Mo: 1.5; W: 1.5; S: 0.014; P: 0.015; ]
WELTEC-H565-S

Ø1,6-6,0
T Z Fe8
MF6-GF-55-GPT
-
-
HARDFACE W
metal cored
flux
after surfacing
52-60
Порошковая проволока марки Велтек-H565-S предназначена для автоматической и полуавтоматической наплавки под флюсом при восстановлении и упрочнении деталей из углеродистых и низколегированных сталей, работающих в условиях трения металла о металл при повышенных температурах, термоциклировании и больших удельных давлениях. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.55; Mn: 1.4; Si: 0.7; Cr: 5.5; Mo: 1.5; W: 1.5; S: 0.014; P: 0.015; ]
WELTEC-H566-G

Ø1,2–2,6
T Z Fe2
MF6-GF-55-GPT
OK Tubrodur 15.50 - с.н. ОК Tubrodur 60 GМ - н.н.
SK 600-G/UTR DUR 600
ROBODUR K 600
metal cored
shielding gas
after surfacing
55-60
Порошковая проволока марки Велтек-H566-G предназначена для автоматической и полуавтоматической наплавки в среде углекислого газа при восстановлении и упрочнении деталей из углеродистых и низколегированных сталей, работающих в условиях трения металла о металл при повышенных температурах, термоциклировании и больших удельных давлениях. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.7; Mn: 1.0; Si: 0.7; Cr: 5.5; Mo: 0.9; S: 0.015; P: 0.013; ]
WELTEC-H570-G

Ø1,6–2,6
T Z Fe3
MF6-GF-50-GPT
-
-
-
metal cored
shielding gas
after surfacing
46-55
Порошковая проволока марки ВЕЛТЕК-Н570-G предназначена для автоматической и полуавтоматической наплавки в среде углеуислого газа деталей, работающих в условиях трения металла о металл при повышенных температурах, термоциклировании и больших удельных давлениях. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.3; Mn: 0.8; Si: 1.0; Cr: 4.0; Ni: 1.1; Mo: 2.5; V: 0.5; W: 2.5; S: 0.014; P: 0.015; ]
Wet-FCW-Sw-25Cr5VMoSi

Ø1,6–3,6
-
SK 500-G
-
-
flux
after surfacing
41-52
Порошковая проволока марки ВеТ ПП-Нп-25Х5ФМС предназначена для механизированной наплавки под флюсом и открытой дугой деталей, работающих в условиях циклической термической нагрузки и интенсивного изнашивания. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.25; Cr: 5.4; Mn: 0.7; Si: 1.1; Mo: 1.2; V: 0.45; S: 0.04; P: 0.04; ]
Wet-FCW-Sw-35W9Cr3SiV

Ø2,6–4,0
-
-
-
-
flux
after surfacing
42-54
Порошковая проволока марки ВеТ ПП-Нп-35В9Х3СФ предназначена для механизированной наплавки под флюсом деталей, работающих в условиях циклической термическойусталости и больших удельных давлений. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.34; Cr: 2.8; Mn: 0.8; Si: 0.6; V: 0.35; W: 9.5; S: 0.04; P: 0.04; ]
Wet-FCW-Sw-35W9Cr3SiV-M

Ø2,6–4,0
-
-
-
-
flux
after surfacing
42-54
Порошковая проволока марки ВеТ ПП-Нп-35В9Х3СФ-М предназначена для механизированной наплавки под флюсом деталей, работающих в условиях циклической термическойусталости и больших удельных давлений. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.34; Cr: 2.8; Mn: 1.2; Si: 0.6; V: 0.35; W: 9.5; S: 0.04; P: 0.04; ]
Wet-FCW-Sw-60W9Cr3SiV

Ø1,6–4,0
-
-
-
-
flux
after surfacing
54-60
Порошковая проволока марки ВеТ ПП-Нп-60В9Х3СФ предназначена для автоматической наплавки под флюсом деталей из углеродистых и низколегированных сталей, работающих в условиях трения металла о металл при повышенных температурах, термоциклировании и больших удельных давлениях. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.6; Cr: 3.1; Mn: 1.2; Si: 0.6; V: 0.42; W: 9.8; S: 0.04; P: 0.04; ]
FCW-Sw-25Cr5VMoSi

Ø1,6–3,6
-
-
-
-
flux
after surfacing
40-51
Порошковая проволока марки ПП-Нп-25Х5ФМС предназначена для механизированной наплавки под флюсом деталей, работающих в условиях циклической термической нагрузки и интенсивного изнашивания. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.25; Cr: 5.4; Mn: 0.7; Si: 1.1; Mo: 1.2; V: 0.45; S: 0.04; P: 0.04; ]
FCW-Sw-25Cr5VMoSiTi

Ø1,6–3,0
-
-
-
-
self- shielding
after surfacing
42-51
Порошковая проволока марки ПП-Нп-25Х5ФМС предназначена для автоматической и полуавтоматической наплавки открытой дугой деталей, работающих при повышенной температуре и больших удельных давлениях . Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.25; Cr: 5.4; Mn: 0.8; Si: 1.1; Mo: 1.1; Ti: 0.2; V: 0.45; S: 0.04; P: 0.04; ]
FCW-Sw-30Cr2Mo2VNi

Ø1,6–3,6
-
-
-
-
flux
after surfacing
42-51
Порошковая проволока марки ПП-Нп-30Х2М2ФН предназначена для механизированной наплавки под флюсом деталей, работающих в условиях циклической термической нагрузки и интенсивного изнашивания. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.29; Cr: 2.4; Mn: 0.7; Si: 0.9; Mo: 2.3; V: 0.6; Ni: 1.2; S: 0.04; P: 0.04; ]
FCW-Sw-30Cr4W2Mo2VSi

Ø1,6–3,6
-
-
-
-
flux
after surfacing
46-52
Порошковая проволока марки ПП-Нп-30Х4В2М2ФС предназначена для механизированной наплавки под флюсом деталей, работающих в условиях циклической термической нагрузки и интенсивного изнашивания. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.32; Cr: 3.7; Mn: 0.8; Si: 1.0; Mo: 2.8; V: 0.45; W: 2.6; S: 0.04; P: 0.04; ]
FCW-Sw-35W9Cr3SiV

Ø1,6–3,6
-
-
-
-
flux
after surfacing
41-54
Порошковая проволока марки ПП-Нп-35В9Х3СФ предназначена для механизированной наплавки под флюсом деталей, работающих в условиях циклической термической усталости и больших удельных давлений. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.34; Cr: 2.8; Mn: 0.8; Si: 0.6; V: 0.35; W: 9.5; S: 0.04; P: 0.04; ]
FCW-Sw-35Cr6Mo2

Ø1,6–3,6
-
-
-
-
flux
after surfacing
44-55
Порошковая проволока марки ПП-Нп-35Х6М2 предназначена для автоматической наплавки под флюсом деталей, работающих в условиях циклической термической нагрузки, больших удельных давлений и интенсивного изнашивания. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.4; Cr: 7.0; Mo: 2.5; Ti: 0.08; V: 0.6; N: 0.03; S: 0.03; P: 0.03; ]
FCW-Sw-45W9Cr3SiV

Ø1,6–3,6
-
-
-
-
flux
after surfacing
42-56
Порошковая проволока марки ПП-Нп-45В9Х3СФ предназначена для механизированной наплавки под флюсом деталей, работающих в условиях циклической термической усталости и больших удельных давлений. Рекомендуется для наплавки на постоянном токе обратной полярности.
[C: 0.38; Cr: 2.8; Mn: 0.8; Si: 0.6; V: 0.35; W: 9.5; S: 0.04; P: 0.04; ]


>